TY - JOUR
T1 - Synthesis of renewable diesel through hydrodeoxygenation reaction from nyamplung oil (Calophyllum Inophyllum oil) using NiMo/Z and NiMo/C catalysts with rapid heating and cooling method
AU - Susanto, Bambang Heru
AU - Prakasa, M. B.
AU - Shahab, M. H.
N1 - Publisher Copyright:
© Published under licence by IOP Publishing Ltd.
PY - 2016/12/12
Y1 - 2016/12/12
N2 - The synthesis of metal nanocrystal was conducted by modification preparation from simple heating method which heating and cooling process run rapidly. The result of NiMo/Z 575 °C characterizations are 33.73 m2/gram surface area and 31.80 nm crystal size. By used NiMo/C 700 °C catalyst for 30 minutes which had surface area of 263.21 m2/gram, had 31.77 nm crystal size, and good morphology, obtained catalyst with high activity, selectivity, and stability. After catalyst activated, synthesis of renewable diesel performed in hydrogenation reactor at 375 °C, 12 bar, and 800 rpm. The result of conversion was 81.99%, yield was 68.08%, and selectivity was 84.54%.
AB - The synthesis of metal nanocrystal was conducted by modification preparation from simple heating method which heating and cooling process run rapidly. The result of NiMo/Z 575 °C characterizations are 33.73 m2/gram surface area and 31.80 nm crystal size. By used NiMo/C 700 °C catalyst for 30 minutes which had surface area of 263.21 m2/gram, had 31.77 nm crystal size, and good morphology, obtained catalyst with high activity, selectivity, and stability. After catalyst activated, synthesis of renewable diesel performed in hydrogenation reactor at 375 °C, 12 bar, and 800 rpm. The result of conversion was 81.99%, yield was 68.08%, and selectivity was 84.54%.
UR - http://www.scopus.com/inward/record.url?scp=85009349953&partnerID=8YFLogxK
U2 - 10.1088/1757-899X/162/1/012009
DO - 10.1088/1757-899X/162/1/012009
M3 - Conference article
AN - SCOPUS:85009349953
SN - 1757-8981
VL - 162
JO - IOP Conference Series: Materials Science and Engineering
JF - IOP Conference Series: Materials Science and Engineering
IS - 1
M1 - 012009
T2 - 2nd International Conference on Chemical Engineering, ICCE 2016
Y2 - 26 October 2016 through 27 October 2016
ER -