TY - JOUR
T1 - Shear bond strength evaluation of chemically-cured and light-cured orthodontic adhesives after enamel deproteinization with 5.25% sodium hypochlorite
AU - Salim, J. C.
AU - Krisnawati,
AU - Purbiati, M.
N1 - Publisher Copyright:
© Published under licence by IOP Publishing Ltd.
PY - 2017/8/30
Y1 - 2017/8/30
N2 - This study aimed to assess the effect of enamel deproteinization with 5.25% sodium hypochlorite (NaOCl) before etching on the shear bond strength (SBS) of Unite (UN; 3M Unitek) and Xihu-BIOM adhesive (XB). Fifty-two maxillary first premolars were divided into four groups: (1) UN and (2) XB according to manufacturer's recommendation and (3) UN and (4) XB deproteinized with 5.25% NaOCl. Brackets were bonded, and a mechanical test was performed using a universal testing machine. The mean SBS value for groups A1, A2, B1, and B2 was 13.51 ±2.552, 14.36 ± 2.902, 16.43 ± 2.615, and 13.05 ± 2.348 MPa, respectively. A statistically significant difference in SBSs was observed between chemically cured groups and between group B (p < 0.05). No statistically significant difference in SBSs was observed between light-cured adhesive groups and between group A (p > 0.05). NaOCl enamel deproteinization before acid etching has a significant effect on the SBS of Unite adhesive, but not on that of the Xihu-BIOM adhesive. Furthermore, a significant difference in the SBS of Unite and Xihu-BIOM adhesives within the enamel deproteinization group was observed in this study.
AB - This study aimed to assess the effect of enamel deproteinization with 5.25% sodium hypochlorite (NaOCl) before etching on the shear bond strength (SBS) of Unite (UN; 3M Unitek) and Xihu-BIOM adhesive (XB). Fifty-two maxillary first premolars were divided into four groups: (1) UN and (2) XB according to manufacturer's recommendation and (3) UN and (4) XB deproteinized with 5.25% NaOCl. Brackets were bonded, and a mechanical test was performed using a universal testing machine. The mean SBS value for groups A1, A2, B1, and B2 was 13.51 ±2.552, 14.36 ± 2.902, 16.43 ± 2.615, and 13.05 ± 2.348 MPa, respectively. A statistically significant difference in SBSs was observed between chemically cured groups and between group B (p < 0.05). No statistically significant difference in SBSs was observed between light-cured adhesive groups and between group A (p > 0.05). NaOCl enamel deproteinization before acid etching has a significant effect on the SBS of Unite adhesive, but not on that of the Xihu-BIOM adhesive. Furthermore, a significant difference in the SBS of Unite and Xihu-BIOM adhesives within the enamel deproteinization group was observed in this study.
UR - http://www.scopus.com/inward/record.url?scp=85029576759&partnerID=8YFLogxK
U2 - 10.1088/1742-6596/884/1/012082
DO - 10.1088/1742-6596/884/1/012082
M3 - Conference article
AN - SCOPUS:85029576759
SN - 1742-6588
VL - 884
JO - Journal of Physics: Conference Series
JF - Journal of Physics: Conference Series
IS - 1
M1 - 012082
T2 - 1st Physics and Technologies in Medicine and Dentistry Symposium, PTMDS 2017
Y2 - 15 July 2017 through 16 July 2017
ER -