PENGARUH DOPING NI TERHADAP RESISTIVITAS SENYAWA LA0.67SR0.33MN1-XNIXO3

Transport properties of lanthanum manganites have been studied. Mixed valence manganites material transport properties changed with doping at La and Mn site. In this study, La0,67Sr0,33Mn1-xNixO3 material was synthesized using sol gel method. These samples were characterized using X-Ray Diffractometer (XRD) to investigate the structure of samples. While the resistivity of samples as a function of temperature was measured using cryogenic magnetometer. XRD result showed that samples were having Rhombohedral structure with R-3c space group and crystallite size smaller than 100 nm. Ni doping have not changed crystal structure but decreased lattice parameter and size of the crystal. Resistivity measurement result showed insulator behavior of the samples and Ni doping enhanced the resistivity of samples.