Microstructure and Structure of LaMnO3/Mn2O3 Film Prepared by Electrodeposition Method

Gede Yudharma, I. N. Rahman, Budhy Kurniawan, Bambang Soegijono, Setia Budi

Research output: Contribution to journalConference articlepeer-review

Abstract

In this study, LaMnO3/Mn2O3 (LMO/MO) film are synthesized using electrodeposition method on SS 316L substrate. The preparation LMO/MO for this electrodeposition was carried out with a concentration of La3+ and Mn2+ between 50-150 mM solution. Electrodeposition results show that with a currents variation of 0.1; 0.5; 1; 2.5 mA, LaMnOHx and MnOHx compounds have been formed. It is also observed that an increasing current are followed by increasing in the composition of the La atom. The good thickness of sample occurs at currents of 1 mA. The sample was then heated at 800°C for 4 hours. The X-ray diffraction (XRD) analysis shows that the sample forms LaMnO3 and Mn2O3 phase with ratio composition of 1.79% and 98.21%.

Original languageEnglish
Article number042052
JournalIOP Conference Series: Materials Science and Engineering
Volume546
Issue number4
DOIs
Publication statusPublished - 1 Jul 2019
Event9th Annual Basic Science International Conference 2019, BaSIC 2019 - Malang, Indonesia
Duration: 20 Mar 201921 Mar 2019

Fingerprint

Dive into the research topics of 'Microstructure and Structure of LaMnO<sub>3</sub>/Mn<sub>2</sub>O<sub>3</sub> Film Prepared by Electrodeposition Method'. Together they form a unique fingerprint.

Cite this