Magnetic behaviors of BaTiO₃-BaFe₁₂O₁₉ nanocomposite prepared by sol-gel process based on differences in volume fraction

Barium titanate BaTiO₃ (BTO) - barium hexaferrite BaFe₁₂O₁₉ (BHF) nanocomposite could be as a raw material of multiferroic. Multiferroic is a class of materials with coupled electric, magnetic and structural order parameters that yield simultaneous effects of ferroelectric, ferromagnetism and ferroelasticity in the same material. This material has potential applications in such as spintronic devices and sensors. This work was an earlier research towards formation of multiferroic material. Knowing magnetic properties that will lead to a better understanding of magnetoelectric coupling in multiferroic material is the objective of this research.The samples were BTO and BHF prepared by sol-gel and then were mixed in bulk system by a conventional techniques in various of volume fraction between BTO: BHF = 1:1; 1:2 and 2:1, then samples were sintered at 925°C for 5, 10 and 15 hours. Composite phase study was carried out using X-Ray Diffraction (XRD). MPS Magnet - Physik EP3 - Permagraph L was used to characterize magnetic properties. XRD results confirm that composite with volume fraction of BTO: BHF = 1:1 with sintering at 925°C for 5 hours consists only of 2 phases BTO and BHF. There is impurity phase BaFe2O4 beside BTO and BHF phases at samples with volume fraction BTO:BHF = 1:2 and 2:1 for longer sintering. Composite with volume fraction of BTO:BHF = 1:1 for 5 hours sintering has a high value of remanent magnetization 0.081 T and the lowest value of intrinsic coersive 333.6 kA/m leading to good characteristics of multiferroic materials.