Investigation on mechanical properties of AlZrCr- A12O 3 nanocomposites fabricated by stir casting

Research output: Contribution to journalConference articlepeer-review

4 Citations (Scopus)

Abstract

Aluminum alloy composite with nano Al2O3 reinforcement will be designed to have good mechanical properties that correspond to its application. The addition of nano Al2O3 in aluminum is to increase strength and stiffness. In this study aluminum matrix made as a master alloy with the addition of zirconium (Zr) and cerium (Ce) to form Al-Zr-Ce alloys which was reinforced with nanoscale alumina particles known as nano aluminum composite which has high strength and stiffness. Master alloy Al-Zr-Ce used as a matrix content of 0.12 wt% Zr and 0.13 wt% Ce, while Al 2O3 nano particles (<100nm) used as reinforcement was various in the range of 0-3 Vf%. Aluminum composite was produced by stirring of molten metal with a rotational speed of 500 rpm at a temperature of 750°C in an inert argon gas environment then characterized both mechanical properties and microstructure analysis. The tensile strength increased with increasing Al2O3 nano particles up to 1 Vf%. Mechanical properties of composites were slightly increased and there was no significant change in elongation and hardness, perhaps due to the non-uniformity distribution or clustering formation of particles in the matrix.

Original languageEnglish
Article number012009
JournalIOP Conference Series: Materials Science and Engineering
Volume58
Issue number1
DOIs
Publication statusPublished - 1 Jan 2014
Event2014 International Conference on Manufacturing, Optimization, Industrial and Material Engineering, MOIME 2014 - Jakarta, Indonesia
Duration: 29 Mar 201430 Mar 2014

Fingerprint Dive into the research topics of 'Investigation on mechanical properties of AlZrCr- A12O 3 nanocomposites fabricated by stir casting'. Together they form a unique fingerprint.

Cite this