Effect of various sintering temperature on resistivity behaviour and magnetoresistance of La0.67Ba0.33MnO3

R. Pratama, Budhy Kurniawan R., Azwar Manaf, M. R. Ramadhan, D. Nanto, S. A. Saptari, A. Imaduddin

Research output: Chapter in Book/Report/Conference proceedingConference contributionpeer-review

2 Citations (Scopus)

Abstract

A detail work was conducted in order to investigate effect of various sintering temperature on resistivity behavior and its relation with the magneto-resistance effect of La0.67Ba0.33MnO3 (LBMO). The LBMO samples were synthesized using solid state reaction. Characterization using X-ray diffraction shows that all LBMO samples have a single phase for each variation. Variation of sintering temperature on the LBMO samples affects its lattice parameters. The resistivity measurement in an absence and under applied magnetic field resulted in a highly significant different values. In one of the sintering temperature variation of LBMO, an increasing resistivity had shown at a low temperature and had reached its maximum value at a specific temperature, and then the resistivity decreases to the lowest value near the room temperature. Similar result observed at higher varieties of sintering temperature but with significant lower maximum resistivity.

Original languageEnglish
Title of host publicationInternational Symposium on Current Progress in Mathematics and Sciences 2015, ISCPMS 2015
Subtitle of host publicationProceedings of the 1st International Symposium on Current Progress in Mathematics and Sciences
EditorsTerry Mart, Djoko Triyono
PublisherAmerican Institute of Physics Inc.
ISBN (Electronic)9780735413764
DOIs
Publication statusPublished - 19 Apr 2016
Event1st International Symposium on Current Progress in Mathematics and Sciences, ISCPMS 2015 - Depok, Indonesia
Duration: 3 Nov 20154 Nov 2015

Publication series

NameAIP Conference Proceedings
Volume1729
ISSN (Print)0094-243X
ISSN (Electronic)1551-7616

Conference

Conference1st International Symposium on Current Progress in Mathematics and Sciences, ISCPMS 2015
CountryIndonesia
CityDepok
Period3/11/154/11/15

Fingerprint Dive into the research topics of 'Effect of various sintering temperature on resistivity behaviour and magnetoresistance of La<sub>0.67</sub>Ba<sub>0.33</sub>MnO<sub>3</sub>'. Together they form a unique fingerprint.

Cite this