LaFeO3 is a material with Perovskite structure which electrical properties got investigated a lot, because as a p-type semiconductor it showed good gas sensing behavior through resistivity comparison. Sr doping on LaFeO3 is able to improve the electrical conductivity through structural modification. Using the Sr atoms doping concentration (x) from 0.1 to 0.4, La1-xSrxFeO3 nanocrystal pellets were synthesized using sol-gel method, followed by gradual heat treatment and uniaxial compaction. Structural analysis from XRD characterization shows that the structure of the materials is Orthorhombic Perovskite. The topography of the sample by SEM reveals grain and grain boundary existence with emerging agglomeration. The electrical properties of the material, as functions of frequency, were measured by Impedance Spectroscopy method using RLC meter. Through the Nyquist plot and Bode plot, the electrical conductivity of La1-xSrxFeO3 is contributed by grain and grain boundaries. It is reported that La0.6Sr0.4FeO3 sample has the most superior electrical conductivity of all samples, and the electrical permittivity of both La0.8Sr0.2FeO3 and La0.7Sr0.3FeO3 are the most stable.