T1 - CORRELATION BETWEEN MORPHOLOGICAL AND FRACTION SIZE OF INTERMETALLIC ON FLUIDITY OF Al-11%Si ALLOY WITH Fe ADDITION
AU - Nanda, Is Prima
AU - Suharno, Bambang
PY - 2010
Y1 - 2010
N2 - Intermetallic morphology influence on the fluidity of alloys Al-11% Si. From the experiments, fluidity in the alloy Al-11% Si were added 0.6, 0.8, and 1.0% Fe, it was found that the higher the Fe content is added to the values decreasing fluidity. On addition of 1% Fe provides the longest phase of intermetallic 50.2 mm, while the shortest intermetallic phase is given by the addition of 0.6% Fe 21.3 mm. In the alloy Al-11% Si with the addition of Fe are generally higher and higher, would produce intermetallic area fraction increased significantly. On addition of 0.6% Fe intermetallic area fraction of 1.01%, while the addition of 0.8% and 1% Fe Fe each area fraction 1.16% and 2.26%.
AB - Intermetallic morphology influence on the fluidity of alloys Al-11% Si. From the experiments, fluidity in the alloy Al-11% Si were added 0.6, 0.8, and 1.0% Fe, it was found that the higher the Fe content is added to the values decreasing fluidity. On addition of 1% Fe provides the longest phase of intermetallic 50.2 mm, while the shortest intermetallic phase is given by the addition of 0.6% Fe 21.3 mm. In the alloy Al-11% Si with the addition of Fe are generally higher and higher, would produce intermetallic area fraction increased significantly. On addition of 0.6% Fe intermetallic area fraction of 1.01%, while the addition of 0.8% and 1% Fe Fe each area fraction 1.16% and 2.26%.
UR - http://ejournal.umm.ac.id/index.php/industri/article/view/568
U2 - 10.22219/JTIUMM.Vol11.No2.112-116
DO - 10.22219/JTIUMM.Vol11.No2.112-116
M3 - Article
SN - 1978-1431
VL - 11
SP - 112
EP - 116
JO - Jurnal Teknik Industri
JF - Jurnal Teknik Industri
IS - 2
ER -