ANALISIS MAMPU BENTUK BAHAN BAKU SELONGSONG MUNISI Cu-Zn 70/30 SETELAH DEFORMASI PADA SUHU 500ºC = ANALYSIS FORMABILITY OF RAW MATERIALS CU - ZN MUNITIONS CASINGS 70/30 AFTER DEFORMATION AT TEMPERATURE 500ºC

casing because both processes have important role to derive raw material into the required form, dimensions and characteristics. Cu-Zn 70/30 alloy is raw material which normally used as munition casing however, its formability after deformation and heat treatment is not widely known. Therefore, this research has an objective to study the effect of deformation at warm temperature on cold formability by introducing thermomechanical controlled processed in warm rolling. Warm rolling have been conducted by double pass reversible method on 25% x 2, 30% x 2, and 35% x 2 at temperature 500oC. Evaluation of formability have been done by limited tensile test up to 20% elongation and full tensile test until rupture. The result of this research indicates that the best formability of Cu-Zn 70/30 is obtained on specimen which are deformed by warm rolling at actual degree of deformation 38.7%. Formability testing result for his specimen under designated warm rolling parameter has an elongation 10 % with strain hardening coefficient 0.00228, average normal anisotropy value 0.5452, and plannar anisotropy value Δr<1 is: -0.42.